BOR-Q-805F
  STARCH BASED COMPOSTABLE RESIN
..

.

.. .
 

  Product Type :
. . Film Blowing Grade Starch Based Compostable Resin
    Compliance with :
   

EN13432 - ASTM D 6400

The degradation ratio 99% in 100 days

   
   
   
     
 

Product Properties :

Granules are in light yellow, with slight starch fragrance, easily absorb moisture and easily decomposed by microbes within 90 days, anti-static, easily colored. Granules come in cylinder or round shape. The processing temperature is lower than that of conventional plastic. Such granules can be directly processed into finish products without adding any other polyolefin materials like PE, PP, PS, PVC, etc.

 

Recommended Applications:

Compostable packaging film. Compostable bags, including shopping bags, garbage bags, pet waste bags, electronic products packing bags, etc.       

 

       

 

Processing Equipment:

Machines, like common film blowing machine, sheet extruder, bag making machine, printers, heat seal machine, etc, can be used to process bio-products. The resin is especially suitable for downward blowing and water-cooling systems.

 

Processing Technology

Using film extruder with a screw of L/D ratio≥281, and the blow-up ratio should be more than 13, which will help to achieve maximum production yield and best film quality.

 

The freshly blown film feels brittle and crisp. Its elongation is fairly low. This is due to the severe dehydration during production. After a 24 hour curing period, it will regain its properties of tensile strength and elongation. Therefore, newly made film needs 24 hours of curing period before further processing like printing or bag-making.

 

Remanks:

Due to the high starch content, the resin easily absorbs moisture. It needs to be stored in a dry environment, and the packaging should be sealed properly to prevent moisture.

 

In case the resin is damp, it should be dried for 2 hours at 80C. During processing, the temperature is correct when the corn starch fragrance can be smelled at the hopper. It can be decomposed into soil friendly substances under a microbial environment within 90 days.

 
 
 
 
 
 
 
 
       

Properties and Data:  BOR-Q805 F

Testing Item

Standard

Unit

Result

Appearance

Q/320113SSD001 - 2002

Light yellow

Density

GB 1033

g/cm3

1.15 1.30

Moisture Content

Q/320113SSD001 - 2002

%

0.5 - 1

Melt Flow Rate

GB3682

g/10 min

2 -5

Tensile strength

GB 1040

MPa

≥15

Breaking Elongation

GB 1040

%

≥350

Bio Substances Content

Q/320113SSSD001 - 2002

%

≥98

n-hexane Extracts

GB/T5009.58

%

≤4.0

Softening Point

GB/1633

C

>70

Degradation rate in 100days

ASTM D6400/EN13432

%

>99

The data for tensile strength and breaking elongation refer to that of finish products.